Question

請問鎂合金的種類有哪些?(越詳細越好)
各種鎂合金的強度,有何差異?
如有相關數據就太棒了!
懇請協助,謝謝!

Answer 1

Chemical  Compositions of Die Casting Magnesium AlloySpec.AlZnMnREZrSi≤Fe≤Cu≤Ni≤OthersTotalAZ91D8.50-9.500.45-0.900.17-0.40——0.050.0040.0150.001—0.30AZ91A8.50-9.500.45-0.90>0.15——0.20—0.080.01—0.30AZ91B8.50-9.500.45-0.90>0.15——0.20—0.250.01—0.30AZ91E8.50-9.500.45-0.900.17-0.50——0.20—0.0150.0010.01—AM60A5.70-6.30—>0.15——0.200.0040.0080.01—0.03AM60B5.60-6.40—0.26-0.50——0.050.0040.0080.0010.01—AM50A4.50-5.30<0.200.28-0.50——0.050.0040.0080.0010.01—AM201.70-2.50<0.20>0.35——0.050.0040.0080.0010.01—AS41A3.70-4.80<0.100.20-0.48——0.60-1.400.0040.0080.0010.01—AZ63A5.50-6.502.70-3.300.15-0.35——0.20—0.200.01—0.30AZ81A7.20-8.000.50-0.900.15-0.35——0.20—0.080.01—0.30AZ817.20-8.500.45-0.90>0.17——0.050.0040.0250.0010.01—AZ92A8.50-9.501.70-2.300.13-0.35——0.20—0.200.01—0.30ZE41A—3.70-4.80>0.151.00-1.750.30-1.000.01—0.030.01—0.30ZE63A—5.50-6.00—2.00-3.000.30-1.000.01—0.030.01—0.30ZK61A—5.70-6.30——0.30-1.000.01—0.030.01—0.30最常見的AZ91AZ91A,B,DAZ91C,EPropertyF TemperF TemperT4 TemperT6 TemperTensile strength, MPa (ksi)230 (33)165 (24)275 (40)275 (40)Tensile yield strength, MPa (ksi)150 (22)97 (14)90 (13)145 (21)Elongation in 50 mm (2 in.), %32.5156Compressive yield strength at 0.2% offset, MPa (ksi)165 (24)97 (14)90 (13)130 (19)Ultimate bearing strength, MPa (ksi)-415 (60)415 (60)515 (75)Bearing yield strength, MPa (ksi)-275 (40)305 (44)360 (52)Hardness, HB63605570Hardness, HRE75666277Charpy V-notch impact strength, J (ft.lbf)2.7 (2.0)0.79 (0.58)4.1 (3.0)1.4 (1.0)

Answer 2

鎂大多存在於菱鎂礦石中，工業上將其所含的氧及氯去除，再還原成鎂，而鎂合金是在鎂中加入鋁、鋅及錳等元素合成而成。鎂合金材質因散熱佳，可阻隔電波干擾、重量輕、不易變形破損，可完全回收，符合環保要求，最早應用在航空業，之後使用範圍逐漸延伸至汽車零件製造業，目前已成功打入筆記型電腦機殼、數位相機、V8錄影機、行動電話、3C產品的外殼市場，甚至未來LCD電視外殼都將使用鎂合金。

鎂的比重約為鋁的2/3，鋅的1/4及鋼的1/5，而鎂合金的比重為1.8，較鋁合金2.7及鋅合金6.7為低，對亟需減重的產業極具吸引力。過去由於製造技術的不足，無發克服強度、熔點等問題，所以應用不廣，但隨著壓鑄技術的進步，半固態射出成型的興起，週邊模具及二次加工廠的配合，鎂合金產業迅速成長。